6061 Aluminum Flat Bar 6061 T-6 is a precipitation hardening aluminum alloy containing magnesium and silicon as its major alloying elements. 6061 has good machinability and good weldability. Typically after welding the properties near the weld are those of 6061-0 a loss of strength of around 80%. The material can be re-heat-treated to SevenTrust -T4 or -T6 temper for the whole piece.

The nominal composition of type 6061 aluminum is 97.9% Al 0.6% Si 1.0%Mg 0.2%Cr and 0.28% Cu. The density of 6061 aluminum alloy is 2.7 g/cm 3 (0.0975 lb/in 3). 6061 aluminum alloy is heat treatable easily formed weld-able and is good at resisting corrosion.

7075 t74/t651 6060 6061 60613 t5/t6 aluminum extruded bar . If you have any questions or good suggestions on our products and site or if you want to know more information about our products please write them and send to us we will contact you within one business day.

Alibaba.com offers 2498 6061 t5 aluminum bar products. A wide variety of 6061 t5 aluminum bar options are available to you such as temper processing service and surface treatment.

Aluminum Extrusion Section Types of aluminum extrusion includes round bars square bars hexagonal bars flat bars aluminum grooves round tubes quadrangular tubes L-shaped aluminum with mass production of customer-specific customized models heat sinks etc. 鋁扁條 Aluminum flat bar 6063-T5、6061-T6、7075-T6 Specification 1/2” * 1/8” 5/8″ * 9.5 3/4” * 1/16” 3/4” * 1/8” 3.

To simplify this article the strength values for this alloy will be taken from T6 tempered 6061 aluminum alloy (6061-T6) which is a common temper for aluminum plate and bar stock. Its modulus of elasticity is 68.9 GPa (10000 ksi) and its shear modulus is 26 GPa (3770 ksi). These values measure the alloy’s stiffness or resistance to deformation and are found in Table 1. Generally this.

Annealed 6061 (6061-O temper) has maximum ultimate tensile strength no more than 150 MPa (22 ksi) and maximum yield strength no more than 83 MPa (12 ksi) or 110 MPa (16 ksi). The material has elongation (stretch before ultimate failure) of 10–18%. To obtain the annealed condition the alloy is typically heated at 415 °C for 2-3 hours. 6061-T4

Aluminum Flat Bar is produced in several alloys 6063T5 and most generally 6061 is used for structural and engineering applications or when welding is required forming bending or corrosion resistance is a concern. 2024 and 7075 are alloys for high strength applications when no welding or very limited forming or bending is required. 6063 is the lowest strength of these alloys but tends to anodize the best and also has the best finishing qualities.

Chalco Aluminum extrude 6063 6061 aluminum flat bar busbar in different diameter however to serve client fast we stock 6063 6061 aluminum flat bar busbar fo...

6063–T5 aluminum is a type of 6063 aluminum. It is furnished in the T5 temper. To achieve this temper the metal is artificially aged until it meets standard mechanical property requirements. T5 was developed as an extrusion alloy with relatively high tensile properties excellent finishing characteristics and a high degree of resistance to corrosion. T5 aluminum alloy is most often found in.